Page 49 - Product Catalog By Zika Welding

49

SILVER RODS FOR COPPER SOLDERING

Item Description Standard Catalog Number Diameter (mm)
Copper-Phosphorus wire with a low silver L-AG2P - FLAT ROD 1,3X3,2X500MM CP 105 TIGSB5%-FLT 1.3X3.25
content. Suitable for filling wide connections.
Suitable for brazing copper and copper
alloys. Operating temperatures between - alley
60 ° C and 150 ° C * Do not use in sulfuric of type and scrambled it to make a ty
environment and on ferrous and nickel alloys.

Bare copper wire - phosphorus with 15% silver BS EN 1044 15 AG BARE WIRE TIGSB15%-30BR 1.6
content that provides high ductility, even
At low temperatures. Suited for soldering
copper and copper alloys. Recommended
for connections with high heat load and
vibration. In common with brazing for
working temperatures between - 70 °
C and 150 ° C *. Do not use in sulfuric
environment and on ferrous and
nonferrous alloys.

Alloy with 20% silver content, without DIN 8513 L AG 20 EN1044-AG 206 TIGSB20%-15 1.5
cadmium. Not sensitive to overheating.
Brazing non-alloyed steels and steels
without nickel alloys and nickel-cast iron
alloys, copper and copper alloys. Fully
color matching with brass. Silicon can
reduce the mechanical properties of
carbon steel. For working temperatures
with a maximum of 200 ° C.
Wires containing cadmium are especially DIN 8513 L Ag 20Cd EN1044 AG 309 TIGSB20%-15B 1.5
useful in spare parts stores for air
conditioning. With a 20% silver content,
overheating of the filler material should
be avoided due to the presence of zinc,
which can create holes and prevent sealing
when overheated. Good ventilation is
recommended for the area in which the
soldering takes place.

An alloy with 30% silver content, without UNI EN ISO 17672:2010-AG 130 TIGSB30%-15 1.5
cadmium and not sensitive to overheating.
Brazing non-alloyed steels and steels
without nickel alloys and nickel-cast iron
alloys, copper and copper alloys. Fully
color matching with brass. Silicon can
reduce the mechanical properties of
carbon steel. For working temperatures
with a maximum of 300 ° C.
Wires containing cadmium are especially DIN 8513 L AG 30CD EN1044 AG 306 TIGSB30%-15B 1.5
useful in spare parts stores for air
conditioning. With a 30% silver content,
overheating of the filler material should
be avoided due to the presence of zinc,
which can create holes and prevent sealing
when overheated. Good ventilation is
recommended for the area in which the
soldering takes place.